 STYLE
50
Carbon yarn packing heavily impregnated
with PTFE dispersion. For severe services in
pumps or valves handling chemicals, solvents and
acids. An ideal packing for paper mill
applications.
Temperature: To 600°F (315°C)
pH: 0-14 Speed: 3000 FPM
Pressure: Pumps-To 500 PSI (35 bar)
Construction: Interlock Braid |
|
 STYLE
90
Carbon yarn packing impregnated with
graphite dispersion. For severe services in pump
and valve applications, including super-heated
steam, acids, alkalis, etc.
Temperature: To 850°F - atmosphere
(455°C)
Temperature: To 1200°F -
steam (650°C)
pH: 0-14 Speed: 4000 FPM
Pressure: Pumps-To 500 PSI (35 bar)
Pressure: Valves-To 2500 PSI (170 bar)
Construction: Interlock Braid
|
 STYLE
154
PTFE packing with
PTFE dispersion. A dense firm packing used in
valve and slow speed pump applications.
Excellent chemical resistance.
Temperature: To 500°F (260°C)
pH: 0-14 Speed: 1000 FPM
Pressure: Pumps-To 300 PSI (20 bar)
Pressure: Valves-To 2000 PSI (140 bar)
Construction: Interlock Braid
|
|
STYLE
154 FDA
Food Grade FDA PTFE filament, food grade,
interlock braid with break-in lube.
Temperature: To 500°F (260°C)
pH: 0-14 Speed: 1500 FPM
Pressure: Pumps-To 300 PSI (20 bar)
Pressure: Valves-To 2000 PSI (140 bar)
Construction: Interlock Braid |
 STYLE
160
Graphite filament packing impregnated
with a graphite dispersion. For severe service
applications where leakage must be held to a
minimum. Excellent chemical resistance.
Temperature: To 850°F (455°C) -
Atmosphere
Temperature: To 1200°F
(650°C) - Steam
pH: 0-14 Speed: 4000 FPM
Pressure: Pumps-To 500 PSI (35 bar)
Pressure: Valves-To 2500 PSI (170 bar)
Construction: Interlock Braid |
|
 STYLE
165
Graphite filled PTFE fiber packing that
improves thermal conductivity and will not
harden. 100% GFO®.
Temperature: To 550°F (285°C)
pH: 0-14 Speed: 4300 FPM
Pressure: Pumps-To 300 PSI (20 bar)
Construction: Interlock Braid
*Trademark of W.L. Gore &
Associates |
 STYLE
165K
Unique packaging combining PTFE graphite
with aramid corners. Aramid corners prevent
rolls and extrusion. Excellenct service packing
in servere pump applications. Widely used in
paper mills
Temperature: To 550°F (285°C)
pH: 2-12 Speed:2500 FPM
Pressure: To 300 PSI (20 bar)
Construction: Interlock Braid |
|
 STYLE
170
Aramid fiber packing with an inert
lubricant. Extremely durable, highly abrasive
resistant packing. Ideal for slurry service.
Temperature: To 500°F (260°C)
pH: 3-11 Speed: 1900 FPM
Pressure: 500 PSI (35 bar)
Construction: Interlock Braid |
 STYLE
182
Spun aramid fiber impregnated with PTFE
dispersion and break-in lubricant. Idel for
valves and pumps in abrasive service..
Temperature: To 500°F (260°C)
pH: 2-12 Speed: 2250 FPM
Pressure: 500 PSI (35 bar)
Construction: Interlock Braid |
|
 STYLE
525T
Premier marine service packing made with
flax fibers and lubricated with PTFE dispersion.
It has low friction and high tensile strength.
Excellent for water service and paper mill
applications.
Temperature: To 250°F (120°C)
pH: 4-9 Speed: 1500 FPM
Pressure: To 200 PSI (15 bar)
Construction: Square Braid |
 STYLE
528
Flax fiber packing lubricated with tallow
and wax. Used for brine, cold water and oil
service. Ideal for marine applications.
Temperature: To 200°F (105°C)
pH: 5-9 Speed: 1200 FPM
Pressure: To 150 PSI (10 bar)
Construction: Square Plaited |
|
 STYLE
531
Flax fiber packing, treated with a
petroleum-based
lubricant and surface graphited
Temperature: To 220°F (105°C)
pH: 5-9 Speed: 1200 FPM
Pressure: To 150 PSI (10 bar)
Construction: Square Braid |
 STYLE
1100CR
Braided from a combination of expanded
flexible graphite (1100TCP) and high strength
carbon fibers (90). Carbon fibers are braided
into the corners to provide anti-extrusion and
better abrasion resistance in tough applicaitons.
Can give virtually leak free performance. 1100CR
was independantly fire tested to API 589 at API
607 temperatures and pressures..
Temperature: To 1250°F (650°C) -
Steam
Temperature: To 1050°F
(565°C) - Atmosphere
pH: 0-14 except strong oxidizers
Speed: 4000 FPM
Pressure: 3000 PSI (200 bar)
|
|
 STYLE
1100 I
Braided from a combination of expanded
flexible graphite and inconel wire. 110 I
retains dimensional stability in high
temperature, high pressure environments, and can
meet most VOC emission control regulations. 1100
I was independantly fire tested to API 589 at
API 607 temperatures and pressures.
Temperature: To 1200°F (650°C) -
Steam
Temperature: To 850°F
(455°C) - Atmosphere
pH: 0-14 except strong oxidizers
Pressure: 3000 PSI (200
bar)
Construction: Interlock Braid |
 STYLE
1152
Special syntex fiber, with each strand
impregnated with PTFE dispersion both prior to
and after braiding. Finished packing also has a
break-in lubricant. An asbestos replacement
packing for general service applications. Good
chemical resistance.
Temperature: To 500°F (260°C)
pH: 0-12 Speed: 2200 FPM
Pressure: To 500 PSI (35 bar)
Construction: Interlock Braid
|
|
 STYLE
1162 IB
Syntex fiber thoroughly impregnated with
PTFE, a break-in lubricant is added for
start-up. An economical PTFE general service
packing. Interlock braid.
Temperature: To 500°F (260°C)
pH: 2-10 Speed: 2000 FPM
Pressure: To 300 PSI (20 bar)
Construction: Interlock Braid |
 STYLE
1190
Special Kynol™ fibers treated with PTFE
and break-in lubricant. This is a
non-contaminating packing for use in paper mills
in almost all pump and valve applications.
Temperature: To 500°F (260°C)
pH: 0-13 Speed: 1500 FPM
Pressure: To 500 PSI (35 bar)
Construction: Interlock Braid
|
|
 STYLE
1398
Syntex fiber packing thoroughly
impregnated with a high temperature lubricant.
Finished packing is surface graphited. An
asbestos replacement packing for general service
use on pumps and valves.
Temperature: To 500°F (265°C)
pH: 4-10 Speed: 1500 FPM
Pressure: To 300 PSI (20 bar)
Construction: Interlock Braid |
 100%
expanded virgin PTFE joint sealant. Maximum
performance gasket material. FDA approved.
Temperature: To 600°F (315°C)
pH: 0-14
Pressure: Pumps-To 3000 PSI (200 bar) |
|
 STYLE
2000
Special meta-aramid fiber with PTFE and
break-in lubricant. Very conformable and
abrasive resistant. Highly resistant to
degradation and chemical attack. For use in
agitators, stock pumps, mixers, etc..
Temperature: To 500°F (260°C)
pH: 4-10 Speed: 1500 FPM
Pressure: To 300 PSI (20 bar)
Construction: Interlock Braid |